SUGGESTED FORMULATIONS

100

2.53

R3200 Red Iron Oxide

665

90.00

UROTUF® F78-M-50

65

10.00

Mineral Spirits

0.7

0.09

Antiskinning Agent (0.2%)

1.6

0.20

6% Cobalt Naphthenate (.03%)

832.3

102.82

TOTAL

Lbs.

Fast Dry Industrial Maintenance Enamel

Gals.

Material

(1) (2)

TD-77004Fast Dry Floor Finish 480-V-1

600

81.0

UROTUF® F78-M-50

150

23.0

Mineral Spirits

0.6

0.08

Skino No. 2 (0.2%)

0.5

0.06

6% Cobalt Naphthenate (.01%)

751.1 104.14

TOTAL

Lbs.

Gals.

Material

(1)

(2)

Analysis: 6.0 75 KU 51.7 45.5 8.35

Pigment Volume Concentration, Percent Viscosity at 25C Percent Solids, Weight Percent Vehicle Solids, Weight Pounds per Gallon

Analysis: C 40.0 7.21

Viscosity at 25C, Gardner-Holdt Percent Solids, Weight Pounds per Gallon

Suppliers: (1) Reichhold

(2) OMG

Suppliers: (1) Pfizer

(2) Reichhold

TYPICAL PERFORMANCE DATA

Viscosity, Stokes

TYPICAL VISCOSITY REDUCTION UROTUF F78-M-50 REDUCED WITH MS

100

10

1

Dry Time Set, Minutes Tack-Free, Finger Sward Hardness 1 Day 1 Week Taber Abrasion Resistance mg Weight Loss, CS-17 Wheels,

17 36

17 38

21 48 85

19 45 85

Typical Film Properties 3 Mil Wet Film, 52% Non-Volatile

    • 0.01

      % Cobalt

    • 0.02

      % Exkin No. 2

1000g, 1000 Cycles

0.03% Cobalt

Compatibility UROTUF® F78-X-50* 50% to 75% F78 Solids

0.1

52

47

42

37

Superior Linseed Oil Z2 Polymerized Linseed Oil Z2 Oxidized Linseed Oil AROPLAZ® 1271 Long Oil Alkyd Bakelite VAGH Vinyl Neville R-12 Nitrocellulose Chlorinated Rubber Phenolic Resin (BR-9400)

C C C C C C C I C

Percent Solids by Weight

C = C o m p a t i b l e I = I n c o m p a t i b l e * U R O T U F ® F 7 8 - M - 5 0 s h o w s s i m i l a r c o m p a t i b i l i t y e x c e p t t h a t s t r o n g s o l v e n t s must be added for resins which are not soluble in mineral spirits.

UROTUF® F78-M-50 AND F78-X-50 (14959-00/14961-00) 2