Scotchcal™ ElectroCut™ Graphic Film 7725

Product Bulletin

Product Description

These cast films are designed to create unique, special effect applications. The dusted crystal film has the uniform appearance of etched glass, the frosted crystal ones have the appearance of sand-blasted glass.

Product Line Window decoration

7725-314 7725-323 7725-324 7725-326 7725-327 7725-331

dusted crystal, translucent, matte, permanent adhesive. frosted rose, translucent, matte, permanent adhesive. frosted crystal, translucent, matte, permanent adhesive. frosted green, translucent, matte, permanent adhesive. frosted blue, translucent, matte, permanent adhesive. frosted gold, translucent, matte, permanent adhesive.

Product Characteristics

These are typical values for unprocessed products. Contact your 3M representative for a custom specification.

Physical & Application Material Surface finish Thickness (film)

Adhesive type Adhesive appearance Liner Adhesion

cast vinyl matte 50 µm (0.05 mm) dusted films 90 µm (0.09 mm) frosted films solvent acrylic, pressure-sensitive white transparent synthetic approx. 17 N/25 mm FTM 1: 180° peel, substrate: glass; cond: 24 h 23°C/50%RH

Application method Applied shrinkage Application temperatu


wet or dry < 0.3 mm +10°C

FTM 14 minimum (air and substrate)

Service temperature Surface type Substrate type

  • -

    29°C to +80°C

flat aluminum, glass, PMMA, PC*, ABS, paint

PC*, PETG*: Might require drying with heat before use

Graphic removal

Hard to remove from supported substrates.

Storage Shelf life

Use within two years from the date of manufacture on the sealed original box. Use within one year after opening the box.

Storage conditions

+4°C to +40°C, out of sunlight, original container in clean and dry area.

Flammability Flammability standards are different from country to country. Ask your local 3M contact for details, please.

3M Europe

Product Bulletin 7725-3x

page 1 of 3